Technical Data Sheet
CarbonX™ CF15 PEKK-A 3D Printing Filament
TDS Rev 2
| Physical Properties | ||
|---|---|---|
| Standard | Unit | Typical Value |
| Density | ISO 1183 | g/cc 1.39 |
| Mechanical Properties | ||
|---|---|---|
| Standard | Unit | Typical Value |
| Tensile Strength, Break | ISO 527 | MPa 110 |
| Tensile Modulus | ISO 527 | MPa 8465 |
| Tensile Elongation, Break | ISO 527 | % 2.5 |
| Flexural Strength | ISO 178 | MPa 142 |
| Flexural Modulus | ISO 178 | MPa 8542 |
| Thermal Properties | ||
|---|---|---|
| Standard | Unit | Typical Value |
| Glass Transition Temperature (Tg) | DSC | °C 165 |
| Melt Temperature (Tm) | DSC | °C 305 |
| Deflection Temperature at 0.45 MPa (66psi) | ISO 75 | °C 275 |
| Electrical Property | ||
|---|---|---|
| Standard | Unit | Typical Value |
| Surface Resistance | ASTM D257 | Ohm/sq >108 |
Disclaimer: The technical data contained on this data sheet is furnished without charge or obligation and accepted at the recipient’s sole risk. This data should not be used to establish specifications limits or used alone as the basis of design. The data provided is not intended to substitute any testing that may be required to determine fitness for any specific use.
- Nozzle: 0.4mm or Larger [Hardened Nozzle]
- Layer Height: 0.25mm [60% of Nozzle Diameter is Ideal]
- Extrusion Multiplier: 0.95-1.0
- Extrusion Temp: 385-400°C
- Print Bed Temp: 120-160°C
- Enclosed Chamber Temp: up to 165°C Ideal
- Drying Recommendations: 140°C for 4-6 hours
For more information, visit www.Rev1Tech.com